Search found 55 matches

by admin
Mon Apr 11, 2022 10:23 am
Forum: solid-solid phase transformations
Topic: Fe_Cu
Replies: 6
Views: 383

Re: Fe_Cu

Dear lv,

What means "not a normal reaction"? According to the results you post, many small nuclei are formed which did not yet reach bigger size due to slow transformation rate.

Bernd
by admin
Thu Mar 31, 2022 12:40 pm
Forum: phase-field model
Topic: Bainite model
Replies: 14
Views: 809

Re: Bainite model

Dear shaojielv,

The crash message does not contain any usable information. Can you please send me your input files (including .GES5)?

Bernd
by admin
Mon Jun 21, 2021 10:16 am
Forum: General Concepts/Other Applications
Topic: secondary development
Replies: 4
Views: 1783

Re: secondary development

Dear shaojielv,

Your topic has been moved to this place because it fits best here. The forum "Topics of the Forum" is dedicated for discussion about the structure and topics of this forum.

Thanks for your understanding.

admin
by admin
Mon Jun 07, 2021 10:53 am
Forum: trouble-shooting
Topic: MICRESS case
Replies: 2
Views: 763

Topic has been shifted

Dear user,

Your topic has been shifted here because it did not fit to the board "MICRESS training".

Thank you for your understanding

Your administrator
by admin
Mon Jun 07, 2021 10:50 am
Forum: solid-solid phase transformations
Topic: MICRESS Training
Replies: 2
Views: 821

Topic has been shifted

Dear user,

Your post has been shifted here because it does not fit to the board "MICRESS training".

Thank you for your understanding

Your administrator
by admin
Wed May 12, 2021 12:06 am
Forum: solidification
Topic: Work of solidification
Replies: 8
Views: 1720

Re: Work of solidification

Hi Lv Shaojie, The reason why you get unexpected positions is the following: (30,0) is just outside the domain, so it is skipped. Instead you get nucleation at (0,0) according to your nucleation type at the defined region... The primary dendrite spacing you observe is defined by these initial positi...
by admin
Tue Feb 09, 2021 5:31 pm
Forum: solid-solid phase transformations
Topic: Cementite instability during fast heating
Replies: 1
Views: 762

Re: Cementite instability during fast heating

Dear Vitoria, Why are you sure that the cementite lamellae should not dissolve? Does it happen below the normal thermal dissolution? I have seen in your input file that you use infinite diffusion for C in bcc, thus the distance of the cementite from the austenite front does not play any role. I gues...
by admin
Fri Feb 14, 2020 3:24 pm
Forum: MICRESS Version 7.0
Topic: Urgent: Important Bug Fix
Replies: 0
Views: 2339

Urgent: Important Bug Fix

Dear all, Unfortunately, we have found a bug in the calculation of the thermal part of the driving force in case of TC-coupling. The bug has been corrected, and the fixed executable can be found in the download directory: https://download.micress.rwth-aachen.de/MICRESS/7.0/ The effects of this bug a...
by admin
Sun Dec 22, 2019 8:37 pm
Forum: post-processing
Topic: Phase Boundary along with plot concentration
Replies: 0
Views: 2172

Re: Phase Boundary along with plot concentration

Dear Seder, Welcome to the MICRESS Forum! Unfortunately, there is no direct function for plotting phase boundaries over composition outputs(. However, there may be indirect ways, depending on your case: - you could use "Content/Operations" and mark all cells with value -1 of the .phas output in your...
by admin
Mon Sep 16, 2019 9:33 pm
Forum: post-processing
Topic: Discuss
Replies: 2
Views: 2080

Re: Discuss

Dear 1Tap,

Please note that links are only allowed in this forum, if they are not commercial. For this reason, your signature has been deleted. However, you may link to your private homepage or to where you are affiliated.

Thank you for your understanding!

admin