Re: Austenite to pearlite transformation in steel
Dear Bernd, I have been trying to simulate pearlite using the conventional approach.However, I am quite uncertain about the types of nucleation seed that would be required for this simulation. Is it appropriate to use cementite as substrate phase in addition to ferrite as the phase of new grains? I ...
- Tue Mar 06, 2012 10:58 am
- Forum: pre-processing
- Topic: switching to keyboard input
- Replies: 1
- Views: 2296
switching to keyboard input
Hi all, I would like to know how to change to interactive keyboard input as it is quite difficult to maintain the proper sequence of commands in the driving file for different cases. I have tried using the keyword "_Switch_" in the driving file as mentioned in the manual but I got an error saying "I...
- Sat Nov 12, 2011 4:53 am
- Forum: solid-solid phase transformations
- Topic: Austenite to pearlite transformation in steel
- Replies: 10
- Views: 10559
Austenite to pearlite transformation in steel
Hi, Although I've got many literature for other types of solid-state transformations using micress, but I havn't got enough material on eutectoid transformations(pearlitic in steel) . How to select appropriate interface mobilities in the case of pearlite evolution? Any information on eutectoid trans...
- Wed Sep 14, 2011 7:21 am
- Forum: phase-field model
- Topic: about IFace and nTupel
- Replies: 1
- Views: 2566
about IFace and nTupel
Hi, I am an UG student and I've started learning MICRESS. I would like to know how exactly is interface data stored in iFace & nTupel or how do I decide the parameters. Also, what would the 'minimal' and 'target' usage parameters would do? Also I would like to know whether there are any other source...