Search found 13 matches
- Mon Aug 08, 2016 7:31 pm
- Forum: pre-processing
- Topic: Microstructure from file
- Replies: 28
- Views: 97830
Re: Microstructure from file
Hello Bernd, I would like to read the initial structure from file. However, since the initial structure I would like to read in is from the out put of another software( Monte Carlo ), I might have to construct the input file by myself. Could you give me any pointers as to what the data requirements ...
- Thu Dec 10, 2015 1:30 am
- Forum: pre-processing
- Topic: Microstructure from file
- Replies: 28
- Views: 97830
Re: Microstructure from file
Hello Bernd,
I think it's about Microstructure file. I tried using .phas file, but it failed.
Thanks,
Raina
I think it's about Microstructure file. I tried using .phas file, but it failed.
Thanks,
Raina
- Fri Nov 20, 2015 9:09 pm
- Forum: pre-processing
- Topic: Microstructure from file
- Replies: 28
- Views: 97830
Re: Microstructure from file
Hello Bernd,
Could you tell me the format of the input file that can be read by Micress?
I would like to make some modification and then use "from_file", but I don't know which type of file can be read by Mrcress.
Thanks,
Raina
Could you tell me the format of the input file that can be read by Micress?
I would like to make some modification and then use "from_file", but I don't know which type of file can be read by Mrcress.
Thanks,
Raina
- Sat Nov 07, 2015 7:07 pm
- Forum: pre-processing
- Topic: Microstructure from file
- Replies: 28
- Views: 97830
Re: Microstructure from file
Thanks Bernd! Your last reply really answered my question. Since I'm not very familiar with "restart", I would like to ask more about this. As you said, when using "restart", all additional grain input will be ignored. However, I'm wondering if I set new phase interaction data, will that be ignored ...
- Thu Oct 22, 2015 6:35 pm
- Forum: pre-processing
- Topic: Microstructure from file
- Replies: 28
- Views: 97830
Re: Microstructure from file
Hello Bernd, As you told me, I used ''restart reset_time" and "overwrite", later it asked me to type in Grain Input. If I continue typing in Grain Input as shown below, what is Micress going to use as initial structure? Read from .rest file or read from Grain Input I typed in? # # Grain input # ====...
- Wed Oct 21, 2015 10:35 pm
- Forum: pre-processing
- Topic: Microstructure from file
- Replies: 28
- Views: 97830
Re: Microstructure from file
Hello Bernd, Thanks for your professional advice, but still It doesn't work. :cry: I don't think ''overwrite'' is a good choice, since it will ask me to type in Phase Data later, and I don't think I'm gonna use that as my initial structure. Therefore, I prefer using ''restart''. However, when I type...
- Wed Oct 21, 2015 6:47 pm
- Forum: pre-processing
- Topic: Microstructure from file
- Replies: 28
- Views: 97830
Re: Microstructure from file
Hello Bernd, I really appreciate your quick response! I tried your second method again and still met some issues that I don't understand. 2.png As shown in above picture, I used .rest file and chose ''append'', but still the simulation end and said the data is compressed which I don't think I compre...
- Wed Oct 21, 2015 2:58 am
- Forum: pre-processing
- Topic: Microstructure from file
- Replies: 28
- Views: 97830
Re: Microstructure from file
Hello, Thanks for your reply for my previous question about how to use the output from one simulation as an input file of another simulation. However, when I implemented your methods, there still exist some issues I can't solve. You provide two solutions. First is save the last file as ASCII file an...
- Thu Oct 01, 2015 3:02 am
- Forum: recrystallisation/grain growth
- Topic: Mobility for austenite grain growth
- Replies: 11
- Views: 14925
Re: Mobility for austenite grain growth
Hello, I'm using Micress ran two simulations. One is for ideal isotropic grain growth and another is for ideal grain growth with texture. For the second simulation, I set initial structure random distributed and the misorientation = 30. For modification for surface energy and mobility, I chose "fact...
- Wed Sep 16, 2015 8:14 pm
- Forum: pre-processing
- Topic: Microstructure from file
- Replies: 28
- Views: 97830
Re: Microstructure from file
Hello, I'm using Micress doing the grain growth simulation. During the simulation, first I would like run the isotropic grain growth and then followed by anisotropic grain growth. I would like to use the ending structure of the isotropic growth as the initial structure of the following anisotropic g...