Hello,
How should the temperature displayed below the microstructure in DP MICRESS?

I tried by doing ANNOTATIONS => Information box => set context
But I don't know the command to set temperature.

Thank you

Regards
Manoj

Hello Bernd,
Thanks for guiding to me for solving this problem
After changing the periodic boundary conditions to ssii there are dendrite formed, but not better
So I will try as you mentioned above by increasing spatial resolution and interface mobility.

Thanking You
Manoj.

Hello Bernd Sorry for the mistake it is actually diffusion coefficents of the concentrations in liquid and bcc which are there in .diff file There is no error showing while reading the .ges5 file in MICRESS I have attached the file which that how I created a .ges5 file using Thermo-Calc 2015b data.i...

Hello Bernd I am struggling to get dendrite for the ternary composition As I mentioned above I have created new ges5 file I have observed that in .TabD all the values are zero and in .diff Diff conc are there and there is no dentrite grow in .con and .phas Input file attached here manoj26.in Thankin...

Hello Bernd
I am Using Micress 6.2 and Thermo- Calc 2015b
Yes I append the mobility data .ges5 file
Yes they compatible with the current MICRESS version
I will try again by creating .ges5 file.

Hello Bernd
I checked my .TabD and .diff there diffusion coefficients are shown NAN.
I have attached .log file

Dear Bernd I am trying to do with temperature gradient and without. In my input file I mentioned the output of .driv is no_out_driv_force I will modify my input file with out.driv and with temp gradient and high cooling rates And I also found that .conc there is no dendrite grow can you help me out ...

Dear Bernd Thanks for helping to find out the problem. Now I modified my input file by removing the 'moving_frame' and '1_d_far_field'. The problem is that there is no secondary dendrite growing is happening. please can you help me out from this problem. I am thinking this is because of my anisotrop...

Hello I am totally new to the Micress and am trying to find out to grow dendrites of Fe -C-Cr alloy from liquid to BCC . But I got a problem after maximum phase1(BCC) fraction again its decreasing and dendrites are forming . I don't why it is happening. I tried for cooling rate of (-50 K/s) and (-1k...