Hello,
How should the temperature displayed below the microstructure in DP MICRESS?
I tried by doing ANNOTATIONS => Information box => set context
But I don't know the command to set temperature.
Thank you
Regards
Manoj
Search found 9 matches
- Thu Feb 16, 2017 11:16 am
- Forum: post-processing
- Topic: To display temparature
- Replies: 1
- Views: 4823
- Fri Jul 15, 2016 8:51 pm
- Forum: solidification
- Topic: soldification from Liquid to Bcc in Fe-C-Cr alloy
- Replies: 14
- Views: 7283
Re: soldification from Liquid to Bcc in Fe-C-Cr alloy
Hello Bernd,
Thanks for guiding to me for solving this problem
After changing the periodic boundary conditions to ssii there are dendrite formed, but not better
So I will try as you mentioned above by increasing spatial resolution and interface mobility.
Thanking You
Manoj.
Thanks for guiding to me for solving this problem
After changing the periodic boundary conditions to ssii there are dendrite formed, but not better
So I will try as you mentioned above by increasing spatial resolution and interface mobility.
Thanking You
Manoj.
- Fri Jul 15, 2016 1:58 pm
- Forum: solidification
- Topic: soldification from Liquid to Bcc in Fe-C-Cr alloy
- Replies: 14
- Views: 7283
Re: soldification from Liquid to Bcc in Fe-C-Cr alloy
Hello Bernd Sorry for the mistake it is actually diffusion coefficents of the concentrations in liquid and bcc which are there in .diff file There is no error showing while reading the .ges5 file in MICRESS I have attached the file which that how I created a .ges5 file using Thermo-Calc 2015b data.i...
- Fri Jul 15, 2016 11:57 am
- Forum: solidification
- Topic: soldification from Liquid to Bcc in Fe-C-Cr alloy
- Replies: 14
- Views: 7283
Re: soldification from Liquid to Bcc in Fe-C-Cr alloy
Hello Bernd I am struggling to get dendrite for the ternary composition As I mentioned above I have created new ges5 file I have observed that in .TabD all the values are zero and in .diff Diff conc are there and there is no dentrite grow in .con and .phas Input file attached here manoj26.in Thankin...
- Thu Jul 14, 2016 5:42 pm
- Forum: solidification
- Topic: soldification from Liquid to Bcc in Fe-C-Cr alloy
- Replies: 14
- Views: 7283
Re: soldification from Liquid to Bcc in Fe-C-Cr alloy
Hello Bernd
I am Using Micress 6.2 and Thermo- Calc 2015b
Yes I append the mobility data .ges5 file
Yes they compatible with the current MICRESS version
I will try again by creating .ges5 file.
I am Using Micress 6.2 and Thermo- Calc 2015b
Yes I append the mobility data .ges5 file
Yes they compatible with the current MICRESS version
I will try again by creating .ges5 file.
- Thu Jul 14, 2016 5:08 pm
- Forum: solidification
- Topic: soldification from Liquid to Bcc in Fe-C-Cr alloy
- Replies: 14
- Views: 7283
Re: soldification from Liquid to Bcc in Fe-C-Cr alloy
Hello Bernd
I checked my .TabD and .diff there diffusion coefficients are shown NAN.
I have attached .log file
I checked my .TabD and .diff there diffusion coefficients are shown NAN.
I have attached .log file
- Thu Jul 14, 2016 7:55 am
- Forum: solidification
- Topic: soldification from Liquid to Bcc in Fe-C-Cr alloy
- Replies: 14
- Views: 7283
Re: soldification from Liquid to Bcc in Fe-C-Cr alloy
Dear Bernd I am trying to do with temperature gradient and without. In my input file I mentioned the output of .driv is no_out_driv_force I will modify my input file with out.driv and with temp gradient and high cooling rates And I also found that .conc there is no dendrite grow can you help me out ...
- Wed Jul 13, 2016 9:12 am
- Forum: solidification
- Topic: soldification from Liquid to Bcc in Fe-C-Cr alloy
- Replies: 14
- Views: 7283
Re: soldification from Liquid to Bcc in Fe-C-Cr alloy
Dear Bernd Thanks for helping to find out the problem. Now I modified my input file by removing the 'moving_frame' and '1_d_far_field'. The problem is that there is no secondary dendrite growing is happening. please can you help me out from this problem. I am thinking this is because of my anisotrop...
- Tue Jul 12, 2016 8:42 am
- Forum: solidification
- Topic: soldification from Liquid to Bcc in Fe-C-Cr alloy
- Replies: 14
- Views: 7283
soldification from Liquid to Bcc in Fe-C-Cr alloy
Hello I am totally new to the Micress and am trying to find out to grow dendrites of Fe -C-Cr alloy from liquid to BCC . But I got a problem after maximum phase1(BCC) fraction again its decreasing and dendrites are forming . I don't why it is happening. I tried for cooling rate of (-50 K/s) and (-1k...