Dear Bernd: I'm sorry for my mistake. Yes, I mean the 'liquidus' temperature. The related nucleation parts of the input file are as follow: # Data for further nucleation # =========================== # Enable further nucleation? # Options: nucleation nucleation_symm no_nucleation [verbose|no_verbose...

Hi Bernd, I use the same project to simulate the solidification process of steel with different initial temperatures (different undercooling). I found that when the initial temperature is 17K below the solidus temperature, the solidification frequency is liquid→ liquid+ferrite→ liquid+ferrite+austen...

Hi Bernd,

Ok, I'll try it. Thanks very much!

Kind regards,
Yaozu

Hi Bernd, Recently I am studying the solute distribution during the solidification process using MICRESS and find some phenomena that confused me. 1) When I simulated the distribution of Al in steel, I found the Al content decrease to a small value (much smaller than the experiment result) during th...

Dear Bernd: It may because my computer is running out of memory. I will try to display the results on another computer. As the same to you, I write results in native format, but I don't know how to use DP_MICRESS for converting them to .vtk format to view with Paraview. Could you please tell me how ...

Dear Bernd: Thanks for your help! I change the position of the initial seed to (0.0.0), then the tip splitting disappears. However, there is a problem with the result. When I observe the output, the .phas and .frac show nothing while .conc can display the simulated result, as shown in the picture. T...

Hi Bernd, I have performed a 3D simulation of dendrite growth with your help. I put the initial seed of the solid phase at the lower-left corner(x=1,y=1,z=1)of the simulation domain and let it grow freely with a temperature gradient and cooling rate. However, after some time I find the structure is ...

Hi, Now I'm simulating the three-dimensional silidification process of steel via MICRESS. However, when I use the 'vtk' option, I can only get the 3d output which should be opened using specialized software, and I cannot observe the intermediate output. If I using the 2d option, I can observe the ou...

Dear Bernd:

Thank you very much for your advice and I will modify my project. Hope to get good results.

Shenyz

Dear Bernd:

I'm so sorry that I was busy with other projects some time ago and ignored the forum....

Now there are the input files (driving file and .ges5), and would you give me more detailed advice.