Dear 1994513kong, Can you please explain what you exactly mean and which is the problem you have? Bernd http://thyrsi.com/t6/367/1536135851x1822614068.png http://thyrsi.com/t6/367/1536135930x-1566673088.png http://thyrsi.com/t6/367/1536135974x1822614068.png Figure 1 is my result.I do want the resul...

Bernd wrote:Dear 1994513kong,

I have written something about this topic here. Maybe it is helpful information for you...

Bernd

Dear Bernd
Thanks for the topic，but I also have question about how to set the repulsion

Hi 1994513kong, Do you mean the repulsion which comes from a translational shift of the ordered lattices of two interacting gamma ' particles? For doing so, you can define an accordingly high interface energy for the gamma ' - gamma ' interaction. Bernd Dear Bernd It's the repulsion which comes fro...

As shown in the topic question，anyone can help me to solve the problem。

Hi 1994513kong, Thanks for sharing the data. I'm still a little confused here on the images you have shared. Are these coming from the same simulation? Following are my suggestions: 1. As far as I understand, you want to have the precipitates in the square shape as show in image 1. Right? But there...

Hi. Can you give a little more details about your simulation set up? Also, if possible, can you give a snapshot of the thickening borders? Do you see any spreading of the interface?? Deepu Dear Depeu I want to get the growing-up like image1 rather than image2.and the setting is listed as follow # T...

Dear Depeu
If possible， can you give me some suggestion？

1994513kong

when the precipitation growing up，Only the border is thickening。I don't know which parameters to change this situation.