MICRESS Forum

Bernd wrote: ↑

Wed May 19, 2021 12:27 pm

Dear SteelOx,

Probably the version of the examples you took from our website do not conform with your current version of MICRESS. Which is the version you currently use? You can see that in the header of the .log -file output.

Bernd

Hi Bernd,

So my micress is 6.402

Cheers

Hi Does anybody have the original examples for T010, T012 Alpha Gamma. I’ve played around with it too much and need to original back. I’ve tried getting to from the website but it doesn’t work when I try and run the example. But i get an error "Please specify a simulation name in the driving file". ...

Hi David, You said before that you already have Thermo-Calc calculations. Just use the same database for MICRESS which you have used with Thermo-Calc. I think your newest version of the TCFE (e.g. TCFE9) should be fine. You cannot edit the .GES-file because it is a binary file. But in the GES_FILES...

Hi SteelOX, ok, so essentially you could start with the quaternary system Fe-Si-B-O. Probably you want to simulate the spherical particles in contact to some atmosphere which contains oxygen, right? Then you need the phases GAS, FCC_A1, BCC_A2, HALITE, and QUARTZ. Which database do you want to use?...

Hi SteelOX: My first question in this regard is: Why do you use the example T009_CastIronDendriteNodules_dri as starting point? This example is quite specific for cast iron with formation of graphite nodules and uses the volume_change option because graphite is creating new volume due to the inters...

Dear SteelOx, Welcome to the MICRESS forum. Unfortunately, we do not have any example input file which is directly suitable for simulation of surface oxidation. I would recommend you to start with some steel example like, perhaps, the A001_Delta_Gamma_dri. This example is for ternary Fe-Cr-C and ha...

Hi all, I am looking to model the surface oxides on the surface of steel and had a few questions about adapting a training example.' I am currently using Example T009 Cast Iron Dendrite nodules and it says adding additional elements it relatively easy, how do i add more elements and change the chemi...

Hi All,

I'm trying just to run the example T009_CastIronDentriteNodules, But i cannot run it unchanged, does anybody know why and how to solve this problem?

Thanks for the help
Regards

David

Thank you for the help,

And how do i modify the examples when the simulation will change?

How do i create a .GES5 file in order to get started.

Apologies im very new at this

Thank you for the help,