Search found 100 matches

by shaojielv
Wed Mar 08, 2023 8:46 am
Forum: solid-solid phase transformations
Topic: stress and strain
Replies: 2
Views: 8260

Re: stress and strain

Dear Bernd,

Thank you very much. According to your suggestion, the problem has been solved.

Shaojielv
by shaojielv
Tue Mar 07, 2023 4:01 pm
Forum: solid-solid phase transformations
Topic: stress and strain
Replies: 2
Views: 8260

stress and strain

I coupled the concentration field and stress in the process of austenitic-ferrite transformation, and the results showed that the stress inhibited the transformation. When I wanted to see the distribution of stress and strain, I found that the stress and strain were 0, and there was no change. What ...
by shaojielv
Fri Oct 21, 2022 2:24 pm
Forum: solid-solid phase transformations
Topic: 3D model
Replies: 1
Views: 4769

3D model

Dear Bernd,

I have built a 3D model. Why is the geometry not found when I open the file, but the program is running normally? Why is this?

lv
by shaojielv
Sat Oct 08, 2022 5:17 am
Forum: solid-solid phase transformations
Topic: element concentrations
Replies: 4
Views: 7893

Re: element concentrations

Dear Bernd,

Thank you very much. The problem has been solved according to your suggestion. Wish you a happy life.

lv
by shaojielv
Fri Oct 07, 2022 4:22 am
Forum: solid-solid phase transformations
Topic: nucleation density
Replies: 2
Views: 5684

Re: nucleation density

Dear Janin,

Thank you very much for your reply. I will complete the calculation of nucleation density according to your description. I am also looking forward to the release of the new version.

lv
by shaojielv
Thu Oct 06, 2022 2:05 pm
Forum: solid-solid phase transformations
Topic: element concentrations
Replies: 4
Views: 7893

Re: element concentrations

Dear, Bernd Thank you very much for your reply, and I will further explain the problem. The concentration in the left picture is 0.1C-1.5Mn, which indicates that the result is very normal. The right picture is the result when I changed the concentration to 0.05C-0.5Mn, and the other parameters have ...
by shaojielv
Wed Oct 05, 2022 3:55 pm
Forum: solid-solid phase transformations
Topic: element concentrations
Replies: 4
Views: 7893

element concentrations

Dear everyone I have a question that I would like to consult with you. In the simulation of solid phase transiformation, everything is very good. However, after I changed a group of different element concentrations, why did the change of phase transiformation result become so big and there was a big...
by shaojielv
Wed Oct 05, 2022 2:35 pm
Forum: solid-solid phase transformations
Topic: nucleation density
Replies: 2
Views: 5684

nucleation density

Dear everyone

How do you evaluate the nucleation density after controlling the number of nucleations by shielding distance and shielding position?
by shaojielv
Mon Jul 18, 2022 3:59 pm
Forum: solid-solid phase transformations
Topic: Austenite → lamellar pearlite
Replies: 9
Views: 10628

Re: Austenite → lamellar pearlite

Dear Ali,

I am very happy to receive your reply, I have sent you a private email, please check it.

lv
by shaojielv
Mon Jun 27, 2022 4:44 pm
Forum: solid-solid phase transformations
Topic: ferritic phase transformation
Replies: 4
Views: 5207

Re: ferritic phase transformation

Or what do you think might be the cause?