Dear Bernd,
Thank you very much. According to your suggestion, the problem has been solved.
Shaojielv
Search found 100 matches
- Wed Mar 08, 2023 8:46 am
- Forum: solid-solid phase transformations
- Topic: stress and strain
- Replies: 2
- Views: 8940
- Tue Mar 07, 2023 4:01 pm
- Forum: solid-solid phase transformations
- Topic: stress and strain
- Replies: 2
- Views: 8940
stress and strain
I coupled the concentration field and stress in the process of austenitic-ferrite transformation, and the results showed that the stress inhibited the transformation. When I wanted to see the distribution of stress and strain, I found that the stress and strain were 0, and there was no change. What ...
- Fri Oct 21, 2022 2:24 pm
- Forum: solid-solid phase transformations
- Topic: 3D model
- Replies: 1
- Views: 5394
3D model
Dear Bernd,
I have built a 3D model. Why is the geometry not found when I open the file, but the program is running normally? Why is this?
lv
I have built a 3D model. Why is the geometry not found when I open the file, but the program is running normally? Why is this?
lv
- Sat Oct 08, 2022 5:17 am
- Forum: solid-solid phase transformations
- Topic: element concentrations
- Replies: 4
- Views: 8576
Re: element concentrations
Dear Bernd,
Thank you very much. The problem has been solved according to your suggestion. Wish you a happy life.
lv
Thank you very much. The problem has been solved according to your suggestion. Wish you a happy life.
lv
- Fri Oct 07, 2022 4:22 am
- Forum: solid-solid phase transformations
- Topic: nucleation density
- Replies: 2
- Views: 6338
Re: nucleation density
Dear Janin,
Thank you very much for your reply. I will complete the calculation of nucleation density according to your description. I am also looking forward to the release of the new version.
lv
Thank you very much for your reply. I will complete the calculation of nucleation density according to your description. I am also looking forward to the release of the new version.
lv
- Thu Oct 06, 2022 2:05 pm
- Forum: solid-solid phase transformations
- Topic: element concentrations
- Replies: 4
- Views: 8576
Re: element concentrations
Dear, Bernd Thank you very much for your reply, and I will further explain the problem. The concentration in the left picture is 0.1C-1.5Mn, which indicates that the result is very normal. The right picture is the result when I changed the concentration to 0.05C-0.5Mn, and the other parameters have ...
- Wed Oct 05, 2022 3:55 pm
- Forum: solid-solid phase transformations
- Topic: element concentrations
- Replies: 4
- Views: 8576
element concentrations
Dear everyone I have a question that I would like to consult with you. In the simulation of solid phase transiformation, everything is very good. However, after I changed a group of different element concentrations, why did the change of phase transiformation result become so big and there was a big...
- Wed Oct 05, 2022 2:35 pm
- Forum: solid-solid phase transformations
- Topic: nucleation density
- Replies: 2
- Views: 6338
nucleation density
Dear everyone
How do you evaluate the nucleation density after controlling the number of nucleations by shielding distance and shielding position?
How do you evaluate the nucleation density after controlling the number of nucleations by shielding distance and shielding position?
- Mon Jul 18, 2022 3:59 pm
- Forum: solid-solid phase transformations
- Topic: Austenite → lamellar pearlite
- Replies: 9
- Views: 11392
Re: Austenite → lamellar pearlite
Dear Ali,
I am very happy to receive your reply, I have sent you a private email, please check it.
lv
I am very happy to receive your reply, I have sent you a private email, please check it.
lv
- Mon Jun 27, 2022 4:44 pm
- Forum: solid-solid phase transformations
- Topic: ferritic phase transformation
- Replies: 4
- Views: 5917
Re: ferritic phase transformation
Or what do you think might be the cause?