Dear Ralph,

I have another query. The phase which is recrystallizing, is there an input which specifies melting point of the phase? How does it decide the recrystallisation start temperature?

Thanks

Hi Ralph, Thanks for the reply, I am using a preprocessed microstructure file, with corresponding Euler angles and dislocation density for recrystallisation modelling in Micress. The grains from orie file look like this in the attachment. Please let me know what could be the problem here. I have run...

Dear Bernd,

I have a basic question, when we input a microstructure file i.e. .txt and a grain info file i.e. .txt (euler angle etc). how does Micress read the info for each grain. Is there some order which exists in which the grain info is being read in correspondence to grain structure.

Khushbu

Hi Bernd,

I am using a grain input file for the initial microstructure, its a deformed microstructure hence the grain boundaries are not very smooth. Could you please suggest how to smoothen them out?

Thanks
Khushbu