Dear Bernd, I am using MICRESS for research on the solidification process of aluminum alloys. Also encountered some problems. First of all, I think that the solidification process should be accompanied by the release of latent heat. I set up several heat extractions, whether it is at 7J/(s·cm3) (fig...

Dear Bernd Thank you for your response to my previous question about the distribution of crystal nuclei. I have used MICRESS to simulate the final solidified structure of the aluminum alloy. I hope it is an equiaxed grain, of course it turned out to be the case. However, there is a problem that the ...

Dear Bernd: Thank you for your answers. I have solved this problem, as you said, the reason for this problem is that the "unit_cell_symm" option is enabled. The command line is specially written by me in order to facilitate the modification of the parameters, I will pay attention to it next time. Th...

Dear Bernd, Best wishes for you. I have used MICRESS to study the structure and composition distribution of isothermally solidified single-grain and multi-grain aluminum alloys. But when I studied the non-isothermal polycrystalline grains, I encountered difficulties: Under the condition of no latent...