Search found 4 matches
- Sun Jan 23, 2022 4:03 pm
- Forum: solidification
- Topic: solidification of Al-alloy (Equiaxed crystal)
- Replies: 1
- Views: 3023
solidification of Al-alloy (Equiaxed crystal)
Dear Bernd, I am using MICRESS for research on the solidification process of aluminum alloys. Also encountered some problems. First of all, I think that the solidification process should be accompanied by the release of latent heat. I set up several heat extractions, whether it is at 7J/(s·cm3) (fig...
- Sun Sep 12, 2021 2:16 pm
- Forum: solidification
- Topic: solidification of Al-alloy ( interface adhesion)
- Replies: 1
- Views: 1094
solidification of Al-alloy ( interface adhesion)
Dear Bernd Thank you for your response to my previous question about the distribution of crystal nuclei. I have used MICRESS to simulate the final solidified structure of the aluminum alloy. I hope it is an equiaxed grain, of course it turned out to be the case. However, there is a problem that the ...
- Tue Sep 07, 2021 10:00 am
- Forum: solidification
- Topic: solidification of Al-alloy (seed_density)
- Replies: 2
- Views: 1068
Re: solidification of Al-alloy (seed_density)
Dear Bernd: Thank you for your answers. I have solved this problem, as you said, the reason for this problem is that the "unit_cell_symm" option is enabled. The command line is specially written by me in order to facilitate the modification of the parameters, I will pay attention to it next time. Th...
- Sun Sep 05, 2021 10:59 am
- Forum: solidification
- Topic: solidification of Al-alloy (seed_density)
- Replies: 2
- Views: 1068
solidification of Al-alloy (seed_density)
Dear Bernd, Best wishes for you. I have used MICRESS to study the structure and composition distribution of isothermally solidified single-grain and multi-grain aluminum alloys. But when I studied the non-isothermal polycrystalline grains, I encountered difficulties: Under the condition of no latent...