Thanks for your kind help, Bernd. This was very helpfull. I will now work on the implementation. Surely this will take some time.

greetings Basti

Dear Bernd, I appreciate your interest in this topic and would like to discuss it with you. As you say: Later you can introduce nitrogen by using a fixed boundary condition on one side of the domain, (or even by putting a gas phase in contact with the correct C:H ratio for acetylene...). This step-b...

Hello everyone. I have the task of simulating the microstructural changes during nitriding of austenitic and duplex Fe-alloys. We have knowledge of how N effect the material. Now we want to set up a simulation supporting our statement before doing further nitriding experiments and microstructural in...