Thanks for your kind help, Bernd. This was very helpfull. I will now work on the implementation. Surely this will take some time.
greetings Basti
Search found 3 matches
- Wed Aug 03, 2022 3:44 pm
- Forum: solid-solid phase transformations
- Topic: Nitriding
- Replies: 4
- Views: 4400
- Tue Aug 02, 2022 12:05 pm
- Forum: solid-solid phase transformations
- Topic: Nitriding
- Replies: 4
- Views: 4400
Re: Nitriding
Dear Bernd, I appreciate your interest in this topic and would like to discuss it with you. As you say: Later you can introduce nitrogen by using a fixed boundary condition on one side of the domain, (or even by putting a gas phase in contact with the correct C:H ratio for acetylene...). This step-b...
- Mon Aug 01, 2022 5:03 pm
- Forum: solid-solid phase transformations
- Topic: Nitriding
- Replies: 4
- Views: 4400
Nitriding
Hello everyone. I have the task of simulating the microstructural changes during nitriding of austenitic and duplex Fe-alloys. We have knowledge of how N effect the material. Now we want to set up a simulation supporting our statement before doing further nitriding experiments and microstructural in...