Dear Ralph
Thank you for your help. I will continue to change the parameters about nucleation and phase interaction to get the second phase.
Thanks again to the people who helped me in forum. I might have given up without your advice.
Best
Rookie
Search found 6 matches
- Wed Oct 19, 2022 4:50 am
- Forum: solidification
- Topic: forrtl: error (65): floating invalid when simulation the second phase
- Replies: 10
- Views: 10770
- Sat Oct 15, 2022 4:44 am
- Forum: solidification
- Topic: forrtl: error (65): floating invalid when simulation the second phase
- Replies: 10
- Views: 10770
Re: forrtl: error (65): floating invalid when simulation the second phase
Dear Bernd I generated a GES5 file with TC2019b in these days, I even changed the type of precipitated phase. Unfortunately, it still get the same result. Thaks for you advice, I willI try the method of the paper and modify some other parameters. There may also be some problems with nucleation param...
- Thu Oct 13, 2022 3:08 am
- Forum: solidification
- Topic: forrtl: error (65): floating invalid when simulation the second phase
- Replies: 10
- Views: 10770
Re: forrtl: error (65): floating invalid when simulation the second phase
Dear Ralph
Sorry, I can only generate a GES5 file with TC2022a .
I will change the parameters as you advice , hope it is useful.
Finally, I want to express my gratitude to all of you. Now I am cofident to solve it .
Best Regards
Rookie
Sorry, I can only generate a GES5 file with TC2022a .
I will change the parameters as you advice , hope it is useful.
Finally, I want to express my gratitude to all of you. Now I am cofident to solve it .
Best Regards
Rookie
- Wed Oct 12, 2022 2:21 pm
- Forum: solidification
- Topic: forrtl: error (65): floating invalid when simulation the second phase
- Replies: 10
- Views: 10770
Re: forrtl: error (65): floating invalid when simulation the second phase
Dear Ralph,
Thanks for your advice. I would like to share my input if you are willing to help me. Here is my GES5 file and my temperture data.
Best wishes
Rookie
Thanks for your advice. I would like to share my input if you are willing to help me. Here is my GES5 file and my temperture data.
Best wishes
Rookie
- Wed Oct 12, 2022 4:59 am
- Forum: solidification
- Topic: forrtl: error (65): floating invalid when simulation the second phase
- Replies: 10
- Views: 10770
Re: forrtl: error (65): floating invalid when simulation the second phase
Dear Bernd Thank you for your reply! I am glad to receive a reply in such a short time. The in-file is shown below. I would appreciate your help if you have time to check it. I got my database from copper based alloys(TCCU3,MOBCU3) in TC 2022a, and micress version number is 6.402(Linux). I hope ther...
- Tue Oct 11, 2022 3:30 pm
- Forum: solidification
- Topic: forrtl: error (65): floating invalid when simulation the second phase
- Replies: 10
- Views: 10770
forrtl: error (65): floating invalid when simulation the second phase
Hello everyone I want to simulation the second phase precipitation process of solidification. However, each time the second phase grain appears, an error is reported as shown below, and I cant find any second phase in the result. I think there are some problem with parameters setting in phase intera...