Hi again Bernd,
I have treid other examples the problem it also for example when irun the AlCu Example the *scr window asks me to press any key but it does not react to the input (which here is simply pressing any key)

Thank in advance,
R,
Mehnoush

Hi Bernd,
i do the simulation on the D drive of my laptop (local) becease i don't have the permition to change any thing on C drive . i transfered the complete example folder to D.
i hope i could understand your question correctly.
Sincerely,
Mehnoush

hi Bernd, I try to run the standard MICRESS examples with MICpad. but when i click on start for simulation it does not calculate anything. the only change that i have made is changing the output file and also to change the directory from c/ to D/. when i open the dri file in MICpad the only thing th...

Thanks Bernd.

Hi Bernd, thanks alot for your reply, it is different from one material to another and also it is dependent on the process parameters. but in general i can be assumed that no microsegregation can be seen. the alloying particles are also distributed homogeneously in the matrix after process. best reg...

Hi Bernd, Then, is it better that i directly start with the steel alloy? the cooling rate is in order of 10^6 . In EDM high heat flux applies in a very small surface during a single discharge. the material constantly is in contact with dielectric (oil or water). in edm is some how like arc welding b...

Hi Bernd, Thanks a lot for your massage. In first step i will try to model solidification of pure iron because i tought it may be easier. but actually the main goal is modelling the microstructure evolution of 42crmo4 during electrical discharge machining (EDM) process. during EDM the material will ...

Hi, I am new in MICRESS, and in the first step i wanted to start my simulation by modeling solidification of IRON. as i looked up in the scripts you give along with the MICRESS software, i found that we should define the interface mobility for different phases. in Literature several methodes for cal...