Search found 1507 matches
- Tue Jul 18, 2023 2:14 pm
- Forum: solidification
- Topic: Solidification of Cu alloys
- Replies: 3
- Views: 9463
Re: Solidification of Cu alloys
Dear A ZU, Welcome to the MICRESS forum. Unfortunately, there are various reasons which can lead to a behavior like what you describe, especially in an old MICRESS version like 6.4. But, generally, I would proceed in the following way: 1.) Check whether your secondary phase has been attributed to th...
- Mon Jul 17, 2023 6:53 pm
- Forum: solid-solid phase transformations
- Topic: solid-solid phase transformation
- Replies: 4
- Views: 11702
Re: solid-solid phase transformation
Dear Kaiyang, What do you mean with "organization effect"? I did not find any obvious problems in your driving file. There may be different numerical reasons why you do not get cementite as expected. Depending on whether you do observe nucleation events for cementite or not, I could imagine the foll...
- Fri Jul 14, 2023 4:13 pm
- Forum: solid-solid phase transformations
- Topic: Initial concentrations
- Replies: 13
- Views: 39996
Re: Initial concentrations
Hi Roscoe,
This seems impossible - maybe you change the file rights of the .dri-file or something similar by your modification?
Or what exactly did you do?
Bernd
This seems impossible - maybe you change the file rights of the .dri-file or something similar by your modification?
Or what exactly did you do?
Bernd
- Thu Jul 13, 2023 10:13 pm
- Forum: solid-solid phase transformations
- Topic: Initial concentrations
- Replies: 13
- Views: 39996
Re: Initial concentrations
Dear Roscoe,
Have you already been able to open and run unchanged example driving files by using the MICpad editor? Then it should also work with the .dri-file which Ralph has created for you.
Best wishes
Bernd
Have you already been able to open and run unchanged example driving files by using the MICpad editor? Then it should also work with the .dri-file which Ralph has created for you.
Best wishes
Bernd
- Sun Jul 02, 2023 10:31 am
- Forum: solid-solid phase transformations
- Topic: Phase determination
- Replies: 1
- Views: 6989
Re: Phase determination
Dear Rosco, In the example input file which you append, the nature of the "austenite" phase is only reflected indirectly by the phase data and phase interaction data which are provided in the input file. That means, it could be any phase with the given properties, and without knowing the purpose of ...
- Wed Jun 07, 2023 4:41 pm
- Forum: solid-solid phase transformations
- Topic: stress
- Replies: 3
- Views: 8940
Re: stress
Dear kaiyang, It seems that the only problem is the extremely high elastic strain of 2% which you apply in z-direction. This leads to numerical problems with the interfaces, in turn somehow leading to grain boundary adhesion at the bcc particles, and very fast movement of the fcc/fcc-grain boundarie...
- Tue Jun 06, 2023 1:55 pm
- Forum: solid-solid phase transformations
- Topic: stress
- Replies: 3
- Views: 8940
Re: stress
Dear kaiyang, Welcome to the MICRESS forum. Without additional context it is not possible to understand what happens hear. You should provide more information about your material and setup, and what you intend to simulate. Optimal would be to also attach or paste your input file here. Just judging f...
- Thu May 25, 2023 2:09 pm
- Forum: solid-solid phase transformations
- Topic: Reading GES5 workspace
- Replies: 1
- Views: 6626
Re: Reading GES5 workspace
Dear waltergarcia, Welcome to the MICRESS Forum! When you define 3 dissolved element in MICRESS, you essentially assume to have a 4-component system, because you need to add the matrix component. On the other hand, when you open a .GES5-file and MICRESS tells you that it contains 3 Elements, this nu...
- Tue May 09, 2023 12:03 pm
- Forum: solid-solid phase transformations
- Topic: Eigenstrain
- Replies: 14
- Views: 53369
Re: Eigenstrain
Dear Jane, please take care that there should be no underscore "_" in the keyword. In MICRESS Version 7.0 the syntax for stress coupling was stressUx: uncoupled (i.e. no effect on driving force) stressCEx: chemo-elastic coupling (i.e. elastic effects on driving force for phase transformation) stress...
- Tue May 02, 2023 11:06 am
- Forum: solid-solid phase transformations
- Topic: Eigenstrain
- Replies: 14
- Views: 53369
Re: Eigenstrain
Dear Jane, If you use stress coupling (stress_mc* or stress _ce*), then elastic stresses may have an effect on the phase transformation. You can see this effect primarily as a mechanical driving force (.dGsp output). The effect can be strong or weak, depending on the size of this driving force (abso...