MICRESS Forum

Dear Bernd,

First of all, thank you for your reply. I will restate my question. I want the small ferrite nucleated at the boundary to be swallowed by the large ferrite grains instead of such extrusion, as shown in the figure below.

I wish you a pleasant life.

lv

hello everyone, In ferritic phase transformation process, the austenite grain boundary and three-phase junction setting, the nucleation process of grow up collision happened between the ferrite phase, and I have set the interaction force between the ferrite phase, but they did not appear the phenome...

Dear Ralph, I have also been learning how to use the experimental data as the initial micro structure, I have saved the experimental pictures in.PGM format through the software GIMP, and I have downloaded the Perl interpreter according to the link you provided to other users, AND I have read the exp...

Dear Ali

I am very excited to see your simulation results. Could I ask you for some advice on the pearlite randomly generated at austenite grain boundaries? If it is convenient, can you share how you do the modeling?

Thank you very much.
Lv

Dear Bernd,

Yes, you are right. If you have time or you are free, can you read my driver file? Could you point out my error through my driver file? Thank you for your support.

lv

Dear Bernd, First of all, I am very happy to receive your reply. After receiving your reply, I began to understand and simulate. After a few days of thinking, I still have some questions that I would like to ask you. According to your reply this time, I think this should be It is the first method yo...

Dear Berrnd,

I'm sorry, I'll attach my file and look forward to hearing from you.

Lv

Dear Bernd, I am really happy to receive your letter, and I am very grateful to you for helping me many times. It is your help that gives me more confidence to persevere. You said that the critical supercooling degree should be less than 0, but I did not have the option of critical undercooling degr...

Dear Bernd, First of all, I am very happy to receive your reply. In your reply, I also understood the establishment of the ferrite recrystallization model. Based on your explanation, I'm going to start the simulation from the second method, and use ferrite as the first matrix phase and reference pha...

Dear Bernd, Yes, that's right, as you said, that's my intention, the first one you mentioned assigning recrystallization energy to ferrite, I think this is a good practice for users, please this How should it be done? Can you talk more about that? I carried out the relevant simulation according to t...