Dear Bernd,
I want to use the MICRESS software to simulate solidification, but I'm not sure exactly what MICRESS can do in the simulation.I hope to get your help if possible.
Finally, I wish you good health and smooth work.
lv Shaojie
Search found 100 matches
- Thu May 06, 2021 4:27 pm
- Forum: solidification
- Topic: Work of solidification
- Replies: 1
- Views: 1194
- Thu Apr 15, 2021 7:56 am
- Forum: phase-field model
- Topic: Multiphase field equation problem
- Replies: 2
- Views: 5962
Re: Multiphase field equation problem
Dear Janin, First of all, thank you very much for your reply. I don't quite understand the external "obstacle" you mentioned in the second question. Could you please explain it in detail?In addition, I can't open the link in question two, so I can't see the article you sent. I hope to get your help....
- Wed Apr 14, 2021 7:11 am
- Forum: phase-field model
- Topic: Multiphase field equation problem
- Replies: 2
- Views: 5962
Multiphase field equation problem
Dear friend, I met some problems in the learning of MICRESS software, and I hope I can get some help here. First , I would like to know how the dynamic equation in MICRESS was derived. The equation can be found in the attachment. When I was deriving the equation, I noticed that it should be derived ...
- Wed Apr 14, 2021 3:58 am
- Forum: solidification
- Topic: Cooling rate
- Replies: 6
- Views: 2987
Re: Cooling rate
Dear Brend,
I am very happy to get your help. I have received the article you sent me, and I will carefully read it. I would like to express my gratitude to you again and wish you a happy life.
Lv Shaojie
I am very happy to get your help. I have received the article you sent me, and I will carefully read it. I would like to express my gratitude to you again and wish you a happy life.
Lv Shaojie
- Tue Apr 13, 2021 3:23 pm
- Forum: solidification
- Topic: Cooling rate
- Replies: 6
- Views: 2987
Re: Cooling rate
Dear Bernd, Thank you very much for your reply. I have a certain understanding of your answer, and I will further understand your answer according to relevant knowledge.I want to learn the influence of cooling rate on dendrite growth in the process of thin slab continuous casting. Just as you said, ...
- Tue Apr 13, 2021 2:21 pm
- Forum: solidification
- Topic: Cooling rate
- Replies: 6
- Views: 2987
Re: Cooling rate
Dear Bernd, I am very happy to receive your reply so soon.I've understood the difference between the two cooling rates you mentioned.I also have a question: the cooling rate mentioned in MICRESS is understood by me to be the cooling rate of metal liquid rather than the solidification rate, I wonder ...
- Tue Apr 13, 2021 7:15 am
- Forum: phase-field model
- Topic: MICRESS simulated precipitation(The second phase)
- Replies: 3
- Views: 4395
Re: MICRESS simulated precipitation(The second phase)
Dear, Bernd, First of all, many thanks for your reply.I want to use the MICRESS software for two simulation processes.The first is to simulate the dendrite growth in the casting process. During the learning process of MICRESS software, I noticed that there are two types of cooling rates, dendrite bo...
- Tue Apr 13, 2021 6:50 am
- Forum: solidification
- Topic: Cooling rate
- Replies: 6
- Views: 2987
Cooling rate
Everybody is good: In the learning process of MICRESS software, I noticed that there were two types of dendrite interface growth rate and cooling rate. I was a little confused as to whether these two cooling rates were the same thing.If not, how exactly should we understand it?And what I'm talking a...
- Tue Apr 13, 2021 6:28 am
- Forum: phase-field model
- Topic: Cooling rate representation method
- Replies: 1
- Views: 3837
Cooling rate representation method
Everybody is good: First of all, as a beginner of Micress software, I am very happy to join our big family.I met some problems in the process of learning. I hope I can get your help. In the process of learning software, I noticed that the cooling rate in MICRESS was expressed directly through a spec...
- Wed Apr 07, 2021 10:37 am
- Forum: phase-field model
- Topic: MICRESS simulated precipitation(The second phase)
- Replies: 3
- Views: 4395
MICRESS simulated precipitation(The second phase)
Dear Sir First was very lucky to join MICRESS forum this big family. As a beginner of MICRESS software, I have a question want to ask you here, because I need to do a grain of precipitation in the second phase of the appeared in the process of growing up, but I didn't relevant resources, hope you ca...