Dear Bernd,
And I think I should add that if I raise the temperature up to about 1700 kelvin the phase transition is basically normal.
lv
Search found 100 matches
- Wed Apr 06, 2022 4:13 pm
- Forum: solid-solid phase transformations
- Topic: Fe_Cu
- Replies: 6
- Views: 10361
- Wed Apr 06, 2022 11:42 am
- Forum: solid-solid phase transformations
- Topic: Fe_Cu
- Replies: 6
- Views: 10361
Fe_Cu
Dear Bernd, Thank you for your reply. I will try my best to solve the transformation of bainite, but I still have some other questions to consult with you. Thank you very much. In addition, I am doing the precipitation of copper-rich phase in Fe_Cu binary alloy, where phase 1 is BCC and phase 2 is F...
- Wed Apr 06, 2022 9:28 am
- Forum: phase-field model
- Topic: Bainite model
- Replies: 14
- Views: 25669
Re: Bainite model
Dear Bernd,
That means I can achieve my goal by adjusting the dynamics parameters. Is that what I understand?
Best wishes.
lv
That means I can achieve my goal by adjusting the dynamics parameters. Is that what I understand?
Best wishes.
lv
- Tue Apr 05, 2022 5:56 am
- Forum: phase-field model
- Topic: Bainite model
- Replies: 14
- Views: 25669
Re: Bainite model
Dear Bernd,
Yes, I understand, but I want ferrite and cementite to grow at the same time, and then treat the cementite as bainite, rather than having the ferrite form first and the cementite form later. What do you think?
lv
Yes, I understand, but I want ferrite and cementite to grow at the same time, and then treat the cementite as bainite, rather than having the ferrite form first and the cementite form later. What do you think?
lv
- Fri Apr 01, 2022 4:22 pm
- Forum: phase-field model
- Topic: Bainite model
- Replies: 14
- Views: 25669
Re: Bainite model
Dear Bernd, I'm sorry I misunderstood what you said. When I read the reply again today, I found out that I made a mistake due to carelessness. I have sent the documents you need to your private email. Please check and I will explain me The main main content, I'm the reference case simulates the tran...
- Thu Mar 31, 2022 3:11 pm
- Forum: phase-field model
- Topic: Bainite model
- Replies: 14
- Views: 25669
Re: Bainite model
Dear Bernd,
Ok, there will also be such an error, attach a picture together.
shaojie lv
Ok, there will also be such an error, attach a picture together.
shaojie lv
- Thu Mar 31, 2022 12:01 pm
- Forum: phase-field model
- Topic: Bainite model
- Replies: 14
- Views: 25669
Re: Bainite model
Dear Bernd,
I can send you the startup files if you want, thank you very much.
shaojie lv
I can send you the startup files if you want, thank you very much.
shaojie lv
- Thu Mar 31, 2022 11:51 am
- Forum: phase-field model
- Topic: Bainite model
- Replies: 14
- Views: 25669
Re: Bainite model
Dear Bernd,
First of all, thank you for your reply. I will try to solve the problem by myself. I have the following error during the calculation process. Can you help me determine the reason?
shoajie lv
First of all, thank you for your reply. I will try to solve the problem by myself. I have the following error during the calculation process. Can you help me determine the reason?
shoajie lv
- Tue Mar 29, 2022 12:47 pm
- Forum: phase-field model
- Topic: Bainite model
- Replies: 14
- Views: 25669
Re: Bainite model
Dear Bernd, Yes, you are right, I do want to simulate bainite transformation, but bainite cannot be represented in thermodynamics, so I want to represent bainite by cementite, which seems to be a wrong idea, can you tell me what phase I should use to represent bainite? I know from literature that ba...
- Tue Mar 29, 2022 10:47 am
- Forum: phase-field model
- Topic: Bainite model
- Replies: 14
- Views: 25669
Bainite model
Dear Bernd, I want to simulate the transformation of austenite to ferrite and bainite by Micress, so that ferrite can nucleate at the austenite grain boundary (nucleation temperature 1000K) and bainite can nucleate at the austenite grain boundary and inside the austenite grain (nucleation temperatur...