separated intervals of simulation
Posted: Mon Dec 21, 2009 3:10 pm
Hallo MICRESS team,
first of all I wish you merry Christmas and a happy new year. Wish you also a big progress in further program development.
Today I have a question about separating the simulation into a few separate temperature profiles.
In my experiment, I quech down the austenite with high cooling rate to ferrite temperature. Then, hold at a constant temperature for gamma-alpha transformation. As my colleage suggests, lots of nucleation should have started since the quenching period. Then the ferrite grows from the settled nuclei during the isothermal transformation.
I still do not have a clue how I can make my simulation into 2 separated simulation interval: first interval-nucleation during high cooling rate + second continuous nucleation and/or growth of ferrite during isothermal transformation. Could you please suggest me?
Thank you very much in advance,
nokkikku
first of all I wish you merry Christmas and a happy new year. Wish you also a big progress in further program development.
Today I have a question about separating the simulation into a few separate temperature profiles.
In my experiment, I quech down the austenite with high cooling rate to ferrite temperature. Then, hold at a constant temperature for gamma-alpha transformation. As my colleage suggests, lots of nucleation should have started since the quenching period. Then the ferrite grows from the settled nuclei during the isothermal transformation.
I still do not have a clue how I can make my simulation into 2 separated simulation interval: first interval-nucleation during high cooling rate + second continuous nucleation and/or growth of ferrite during isothermal transformation. Could you please suggest me?
Thank you very much in advance,
nokkikku