it would be nice if you change your examples for the next release based on my case.
I have one more question about the kinetic transition in micress.
To my understanding, MICRESS in the "standard" mode should be possible to predict the transition from nple to ple if the cell size is small enough (smaller than the thickness of spike) . Am I right?
kind regards
Hao
Bernd wrote:Dear Hao,
Meanwhile, I analyzed the problem with "para" and found some conceptional issues which make it go "too fast", leading to the problem you described. In the next MICRESS version (6.2), the errors will be removed.
If you urgently need a fix, I can send you a corresponding executable. But the "paraTQ" and "nple" models are working correctly, so it should be fine for you...
By the way, your modifications inspired me to improve our standard example! With your permission, I will change our examples for the next release according to your case (with respect to the higher C and Mn compositions and to a constant temperature rather than a constant cooling rate)...
Best regards
Bernd