Re: Ferrite / Cemenite to Austenite
Posted: Tue Jul 06, 2021 9:22 am
Dear Bernd,
thank you so much for your nice reply.
But I want to study on the influence of heat-treatment on the lammela spacing, it means I need to simulate cementite and ferrite phases instead of pearlite phase as a chessboard like pattern. Do you think it is possible?
Further, for the second heat-treatment I have changed all interface energy to the same value but there is not still any growth.
Best regards,
Ali
thank you so much for your nice reply.
But I want to study on the influence of heat-treatment on the lammela spacing, it means I need to simulate cementite and ferrite phases instead of pearlite phase as a chessboard like pattern. Do you think it is possible?
Further, for the second heat-treatment I have changed all interface energy to the same value but there is not still any growth.
Best regards,
Ali