Length of different grain boundaries
Posted: Tue Jul 07, 2015 1:12 am
Hello,
Now I'm trying to use Micress to simulate the grain growth with different boundary mobilities.
In this simulation, I set an threshold angle. When the misorientation is larger than the threshold angle, the mobility of the grain boundary is M1. When the misorientation is smaller than the threshold angle, the mobility is 0.1M1. The initialization of the microstructure is random, and I need to know the ratio of high mobility to low mobility at t=0s. Therefore, the boundary lengths of different misorientations are needed.
I'm wondering would it be possible for Micress to give me a output file of microstructure just like shown in the attached Figure.1? So that I can write a short code to read the length of the grain boundary.
This is so far that I thought. If you have a better method, please let me know.
Regards,
Raina
Now I'm trying to use Micress to simulate the grain growth with different boundary mobilities.
In this simulation, I set an threshold angle. When the misorientation is larger than the threshold angle, the mobility of the grain boundary is M1. When the misorientation is smaller than the threshold angle, the mobility is 0.1M1. The initialization of the microstructure is random, and I need to know the ratio of high mobility to low mobility at t=0s. Therefore, the boundary lengths of different misorientations are needed.
I'm wondering would it be possible for Micress to give me a output file of microstructure just like shown in the attached Figure.1? So that I can write a short code to read the length of the grain boundary.
This is so far that I thought. If you have a better method, please let me know.
Regards,
Raina